用碱从低品位氧化锌矿石中浸出锌
更新日期:2021-05-26     浏览次数:269
核心提示:摘要研究了用氢氧化钠溶液从某低品位氧化锌矿石中浸出锌,考察了反应温度、反应时间、初始碱浓度、搅拌速度等对锌浸出的影响。结果表明:氢氧化钠浓度增

摘要 研究了用氢氧化钠溶液从某低品位氧化锌矿石中浸出锌,考察了反应温度、反应时间、初始碱浓度、搅拌速度等对锌浸出的影响。结果表明:氢氧化钠浓度增大有利于矿石中的锌转化成可溶性Na2Zn(OH)4;在反应温度65℃、初始碱浓度4 mol/L、液固体积质量比10/1、搅拌速度300 r/min条件下浸出120 min,锌浸出率达90.08%。此工艺为低品位氧化锌矿石的资源化提供了一种可供选择的方法。 Leaching of zinc from low-grade zinc oxide ore using sodium hydroxide solution was investigated.Effects of temperature,reaction time,initial sodium hydroxide concentration and agitation rate on leaching rate of zinc were examined.The results show that increasing alkali concentration is beneficial to format soluble compound Na2Zn(OH)4.Under the optimal conditions of temperature of 65℃,reaction time of 120 min,liquid volume-to-solid mass ratio of 10/1,initial alkali concentration of 4 mol/L and agitation rate of 300 r/min,zinc leaching rate is 90.08%.The process provides an alternative method for leaching of zinc from low-grade zinc oxide ore.
作者 袁杰 熊顺龙 吴兴敏 庞林 YUAN Jie;XIONG Shunlong;WU Xingmin;PANG Lin(Liupanshui Normal University,Guizhou 553004,China)
机构地区 六盘水师范学院
出处 《湿法冶金》 CAS 北大核心 2021年第2期102-105,128,共5页 Hydrometallurgy of China
基金 国家自然科学基金青年基金资助项目(51904150) 贵州省科技计划项目(黔科合基础[2020]1Y225) 贵州省普通高等学校科技拔尖人才项目(黔教合KY字[2019]056) 六盘水市科技计划项目(52020-2018-0304,52020-2019-05-09) 六盘水师范学院科技创新团队项目(LPSSYKJTD201801,LPSSYKJTD201905) 六盘水师范学院重点学科建设项目(LPSSYZDPYXK201708) 卓越工程师培养计划项目(LPSSYzyjypyjh201801)。
关键词 低品位 氧化锌矿石 氢氧化钠 浸出 low-grade zinc oxide ore sodium hydroxide leaching zinc